Alkali activation of dif ferent type of ash as a production of combustion process

Presented study deals with the final struc ture and radiological properties of different fly-ash based geopolymers. Lig nite fly-ash (lignite Kolubara – Ser bia) and wood fly ash were obtained in combustion process together with commercial fly-ash. Synthesis of the geopolymers was con ducted by mixing fly-ash, sodium silicate solution, NaOH and water. The sam ples were strength ened 60 °C for 48 hours af ter stay ing at room temperature in covering mold for 24 hours. The X-ray dif frac tion, Fou rier trans form in fra red and SAM mea sure ments were conducted on the sam ples af ter 28 days of geopolymerization pro cess. The X-ray dif frac tion measurements of lignite fly-ash sam ples show anhydrite as the main constituent, while wood fly-ash samples consist of cal cite, albite and gypsum minerals. Besides determination of physicochemical properties, the aim of this study was radiological characterization of lignite fly-ash, wood fly-ash and the obtained geopolymer products. Ac tiv ity con cen tra tion of 40 K and radionuclides from the 238 U and 232 Th decay series, in ash sam ples and fly-ash based geopolymers, were determined by means of gamma-ray spectrometry, and the absorbed dose rate, D, and the annual effective dose rate, E, were calcu lated in accordance with the UNSCEAR 2000 report.